Microstructural effect on near-neutral pH stress corrosion cracking resistance of pipeline steels

✍ Scribed by J. T. Bulger; B. T. Lu; J. L. Luo

Publisher
Springer
Year
2006
Tongue
English
Weight
373 KB
Volume
41
Category
Article
ISSN
0022-2461

No coin nor oath required. For personal study only.

πŸ“œ SIMILAR VOLUMES

Electrochemical corrosion behavior of X8
Electrochemical corrosion behavior of X80 pipeline steel in a near-neutral pH solution
✍ H. B. Xue; Y. F. Cheng πŸ“‚ Article πŸ“… 2010 πŸ› John Wiley and Sons 🌐 German βš– 390 KB

## Abstract In this work, the electrochemical corrosion behavior of X80 pipeline steel was investigated in a near‐neutral pH solution using electrochemical impedance spectroscopy (EIC) and photo‐electrochemical (PEC) measurements as well as X‐ray photo‐electron spectroscopy (XPS) technique. The eff

On the resistance of duplex steel to str
On the resistance of duplex steel to stress corrosion cracking
✍ Prof. Dr.-Ing. VladimΓ­r Číhal πŸ“‚ Article πŸ“… 1992 πŸ› John Wiley and Sons 🌐 German βš– 457 KB πŸ‘ 1 views

## Abstract The paper gives the results of tests carried out into the stress corrosion cracking in duplex stainless steel (Type 02Cr22Ni5Mo3N, W.Nr. 1.4462); this grade is characterized by high resistance to intergranular corrosion, while resistance to stress corrosion cracking may be impaired by t

Effect of applied potentials on stress c
Effect of applied potentials on stress corrosion cracking of X70 pipeline steel in alkali solution
✍ Liang Zhang; Xiaogang Li; Cuiwei Du; Yizhong Huang πŸ“‚ Article πŸ“… 2009 πŸ› Elsevier Science βš– 666 KB

Stress corrosion cracking (SCC) behavior of X70 pipeline steel in alkali solution at different applied potentials was investigated using slow strain rate testing (SSRT). Morphology of X70 pipeline steel fracture surface at different applied potentials was observed by scanning electron microscope (SE

Corrosion behavior of API 5L X-60 pipeli
Corrosion behavior of API 5L X-60 pipeline steel exposed to near-neutral pH soil simulating solution
✍ A. Benmoussa; M. Hadjel; M. Traisnel πŸ“‚ Article πŸ“… 2006 πŸ› John Wiley and Sons 🌐 German βš– 166 KB

Steel gas pipelines are exposed externally to damage by surface corrosion and cracking phenomena. They are the main deterioration mechanism under coating failure and cathodic protection (CP) that can reduce the structural integrity of buried gas transmission pipelines where the soil aggressiveness a