Microhardness and microstructural evolution in pure nickel during high-pressure torsion

✍ Scribed by A.P Zhilyaev; S Lee; G.V Nurislamova; R.Z Valiev; T.G Langdon

Book ID
114386605
Publisher
Elsevier Science
Year
2001
Tongue
English
Weight
464 KB
Volume
44
Category
Article
ISSN
1359-6462

No coin nor oath required. For personal study only.

πŸ“œ SIMILAR VOLUMES

Microstructural evolution in commercial
Microstructural evolution in commercial purity aluminum during high-pressure torsion
✍ A.P. Zhilyaev; K. Oh-ishi; T.G. Langdon; T.R. McNelley πŸ“‚ Article πŸ“… 2005 πŸ› Elsevier Science 🌐 English βš– 267 KB

An investigation was conducted to evaluate the microstructural evolution occurring in disks of commercial purity aluminum processed by high-pressure torsion (HPT) under constrained conditions. Microhardness measurements were taken to assess the variation in hardness across the diameters of disks sub

Microstructures and microhardness of an
Microstructures and microhardness of an aluminum alloy and pure copper after processing by high-pressure torsion
✍ Zenji Horita; Terence G. Langdon πŸ“‚ Article πŸ“… 2005 πŸ› Elsevier Science 🌐 English βš– 230 KB

Experiments were conducted on an Al-3 wt.% Mg-0.2 wt.% Sc alloy and pure Cu to evaluate the effect of high-pressure torsion (HPT). The results show that very substantial grain refinement is achieved in both materials with as-strained grain sizes of ∼150 and ∼140 nm, respectively. Microhardness measu