Abstract
Drawing of mats of linear polyethylene single crystals prepared from dilute solution is possible at temperatures above about 90Β°C. The structure and properties of the drawn specimens are much different from those ordinary drawn bulk polymer. Drawn mats have been investigated by differential scanning calorimetry. The characteristic experimental results are: (a) a broad melting curve, (b) considerable superheating depending on the rate of heating, (c) constancy of the melting point and the heat of fusion with annealing, (d) deviation from the relation between the heat of fusion and the density obtained for the drawn bulk specimens, (e) appearance of two melting peaks in samples annealed at temperatures above about 130Β°C. These results imply that the structure of the drawn mat is characterized by a larger number of the tie chains connecting the neighboring crystals (the structure postulated in earlier papers) than is the case in ordinary drawn bulk polymer. It can be concluded that the transformation of a fringed micellar type of structure to the folded lamellar structure may be difficult during annealing unless crystals melt and then recrystallize during cooling.