Mechanism of stress corrosion cracking of steel in H2S

✍ Scribed by Wu-Yang Chu; Shi-Qun Li; Jhug-Zuor Tien

Publisher
Elsevier Science
Year
1982
Tongue
English
Weight
104 KB
Volume
16
Category
Article
ISSN
0013-7944

No coin nor oath required. For personal study only.

✦ Synopsis

The dynamical processes of the nucleation and propagation of stress corrosion cracking (SCC) of low-alloy steels with a wide range of tensile strength in gas and aqueous solution of HZ.7 were followed metallographically by using a polished WOL type constant deflection specimen. The results show that if

πŸ“œ SIMILAR VOLUMES

Nucleation mechanism of stress corrosion
Nucleation mechanism of stress corrosion cracking from notches
✍ Y. Hirose; T. Mura πŸ“‚ Article πŸ“… 1984 πŸ› Elsevier Science 🌐 English βš– 850 KB

Crack nucleation mechanism of hydrogen assisted cracking at notched cracks in aqueous solutions is investigated, using the compact type specimens with various notch radius in low-tempered 4340 steel. A detached crack initiates at some distance ahead of the notch root. The crack nucleation at the not

Stress corrosion cracking of explosion w
Stress corrosion cracking of explosion welded steel-aluminum joints
✍ M. Czechowski πŸ“‚ Article πŸ“… 2004 πŸ› John Wiley and Sons 🌐 German βš– 281 KB

## Abstract The article presents the test results of stress corrosion resistance of explosion welded steel‐aluminum elements. The tests were carried out by means of the slow strain rate test (10^βˆ’6^ s^βˆ’1^) in air and artificial sea water. The following parameters were measured: tensile strength, ti

On the resistance of duplex steel to str
On the resistance of duplex steel to stress corrosion cracking
✍ Prof. Dr.-Ing. VladimΓ­r Číhal πŸ“‚ Article πŸ“… 1992 πŸ› John Wiley and Sons 🌐 German βš– 457 KB πŸ‘ 1 views

## Abstract The paper gives the results of tests carried out into the stress corrosion cracking in duplex stainless steel (Type 02Cr22Ni5Mo3N, W.Nr. 1.4462); this grade is characterized by high resistance to intergranular corrosion, while resistance to stress corrosion cracking may be impaired by t

Mechanism of corrosion fatigue crack pro
Mechanism of corrosion fatigue crack propagation in high strength steels
✍ Nakasa Keijiro; Takei Hideo; Itoh Hisashi πŸ“‚ Article πŸ“… 1983 πŸ› Elsevier Science 🌐 English βš– 922 KB

The crack propagation velocity in corroGon fatigue (du/dN), were measured on the Ni-Cr-Mo steel quenched and tempered at 473 or 773 K. The steel with high sensitivity to delayed failure reveals the largest (du/dN), under square load and the smaller (da/dN), under positive saw tooth load. The frequen