In this paper, the experiments of tensile and flexural tests were carried out on composites made by reinforcing jowar as a new natural fibre into polyester resin matrix. The samples were prepared up to a maximum volume fraction of approximately 0.40 from the fibres extracted by retting and manual process, and compared with established composites like sisal and bamboo developed under similar laboratory conditions. Jowar fibre has a tensile strength of 302 MPa, modulus of 6.99 GPa and an effective density of 922 kg/m 3 . It was observed that the tensile strength of jowar fibre composite is almost equal to that of bamboo composite, 1.89 times to that of sisal composite and the tensile modulus is 11% and 45% greater than those of bamboo and sisal composites, respectively at 0.40 volume fraction of fibre. The flexural strength of jowar composite is 4%, 35% and the flexural modulus is 1.12 times, 2.16 times greater than those of bamboo and sisal composites, respectively. The results of this study indicate that using jowar fibres as reinforcement in polyester matrix could successfully develop a composite material in terms of high strength and rigidity for light weight applications compared to conventional sisal and bamboo composites.