Martensitic transformations have been studied in splat cooled samples of 8n Au-60 at.% Cd alloy. A vertical shock-tube apparatus was used to quench the molten alloy from various controlled temperatures in the liquid state to room temperature, the quenching rate being of the order of lO'"C/sec. The splat cooled samples were studied by the use of X-ray and electron diffraction 5s well as transmission electron microscopy. It was found that quenching, even at this high speed, from temperatures as high as 300ยฐC above the melting point of this alloy did not 8ffect its long range order. Furthermore, the martenaitic transformation temperature was suppressed in the splat cooled s8mples, and the high temperature #?-phase CsCl type structure persisted. This metastable structure w5s then found to decompose isothermally at room temperature into three morphologically and crystsllographically different maatensitic phases. Excellent resolution of the martensitic fine structure w8s obtained by this splat cooling technique.
TRANSFORMATIONS
MARTENSITIQUES DANS UN ALLIAGE Au-50 % AT.Cd REFROIDI PAR PROJECTION Les transformations martensitiques ont Qte etudiees dans des Bchantillons d'5lli8ge Au-50 %Cd refroidi par projection. Un appareil tubulaire a Bte utilise pour tremper l'alliage fondu 5 partir de differentes temperatures bien determinees du liquide jusqu'5 la temperature ambiante, la vitesse de trempe Btant de l'ordre de lO"C/sec. Les Bchantillons obtenus ont 6th etudies p5r diffraction des rayons X, diffraction Blectronique et microscopic itlectronique par transmission. Les auteurs ont trouve que 15 trempe, m6me a cette grande vitesse et a partir de temperatures aussi Blevees que 300ยฐC au dessus du point de fusion, n'affecte pas l'ordre 5 grande distance d8ns l'alliage. En outre, dana ces Bchantillons, on ass&e 8, la disparition de la temperature de transformation martensitique, et la structure du type CsCl de 15 phase /l existant aux hautes temperatures persiste. Les auteurs ont trouve que cette structure metastable subit une decomposition isotherme 5 temperature ambiante et se transforme en trois phases m8rtensitiques morphologiquement et cristallographiquement differentes. Une excellente resolution de la structure fine martensitique 5 Bte obtenue par la technique du refroidissement par projection. MARTENSIT-UMWANDLUNGEN IN EINER KLATSCHGEKUHLTEN Au-50 AT. % Cd-LEGIERUNG In klatschgekiihlten Proben einer Au-50 At. 'A Cd-Legierung wurden martensitische Umwandlungen untersucht. In einer entsprechenden Apparatur wurde die geschmolzene Legierung von verschiedenen Temperaturen auf Raumtemperatur abgeschreckt ; die Abschreckgeschwindigkeit war von der Gr613enordnung 107'"C~sec. An den klatschgekuhlten Proben wurden Rontgen-und Elektronenbeugungsexperimente durchgeftihrt ; auBerdem wurden sie im Elektronenmikroskop untersucht. Es wurde festgestellt, da6 Abschrecken dieser Legierung von Temperaturen bis zu 300ยฐC iiber ihrem Schmelzpunkt aelbst bei diesen hohen Abschreckgeschwindigkeiten auf ihre Fernordnung keinen Einflu6 hatte. Ferner wurde gefunden, dalj die Temperatur der martensitischen Umwandlung beim Klatschkiihlen erniedrigt wurde und die Hochtemperatur-B-Phase mit CsCl-Struktur erhalten blieb. Diese metastabile Struktur wandelte sich dann isotherm bei Raumtemperatur in drei morphologisch und kristallographisch verschiedene martensitische Phasen urn. Mit Hilfe dieser Klatschktihlmethode wurde eine sehr gute AuflGsung der martensitischen Feinstruktur erreicht.