โ Scribed by R.J Arsenault
No coin nor oath required. For personal study only.
The low-temperature creep characteristics of a iron were studied. The activation energy and activation volume were measured directly by differential temperature, strain rate, and stress techniques. The activation energy and volume were independent of temperature in the range 123-253"K, at a constant effective stress. The activation energy and volume were found to be a function of effective stress, but independent of gram size and 'interstitial impurity content.
The activation volume is independent of strain rate in the range lo-s-l/min.
The activation volume was a function of strain, at 303OK it increases with increasing strain and then remains constant, at 194ยฐK it is independent of strain, and at 77ยฐK it decreases with increasing strain. The experimental results were examined in terms of three proposed rate controlling mechanisms, and problems exist in analyzing the results in terms of all three mechanisms. FLUAGE A BASSE TEMPERATURE DU FER ALPHA L'auteur a Btudie les caracteristiques du fluage it basse temperature du fer alpha. 11 a mesure l'energie d'activation et le volume d'activation en faisant varier la temperature, la vitesse de deformation et la containte appliquee. L'energie d'activation et le volume d'activation sont independants de la temperature dans la gamme 123-253'K, It containte constente. L'energie d'activation et le volume d'activation sont fonction de la contra&e effective, mais ne dependent pas de la dimension du grain et de la teneur en impure& interstitielles. Le volume d'activation est independant de la vitesse de deformation dans la gamme de lo-5-l/min. Le volume d'activation est fonction de la deformation: a 303"K, il augmente avec la deformation et reste ensuite constent; a 194"K, il en est independant; it 77"K, il diminue quand la deformation augmente. L'auteur discute ensuite ces resultats experimentaux en les mettant en relation aveo trois mecanismes proposes pour expliquer le fluage a basse temperature; cette discussion montre que les resultats trouves ne peuvent s'expliquer completement par aucun de ces trois mecanismes. TIEFTEMPERATUR-KRIECHEN VON ALPHA-EISEN Das Tieftemperatur-Kriechen von a-Eisen wurde untersucht. Aktivierungsenergie und Aktivierungsvolumen wurden direkt mittels Differentialtechniken fur Temperatur, Verformungsgeschwindigkeit und Spannung gemessen. Aktivierungsenergie und-Volumen waren-bei konstanter effektiver Spannungim Bereich 123253OK unabhangig von der Temperatur. Aktivierungsenergie und-Volumen hingen von der effektiven Spannung ab, jedoch nicht von der KorngrGlIe und dem Gehalt an Zwischengitter-Verunreinigungen. Das Aktivierungsvolumen hangt im Bereich 10e5-1/ min nicht von der Verformungsgeschwindigkeit ab. Das Aktivierungsvolumen war eine Funktion der Verformung: bei 303OK nimmt es mit der Verformung zunachst zu, urn dann konstant zu bleiben, bei 194ยฐK ist es unabhangig von der Verformung und bei 77ยฐK nimmt es bei steigender Verformung ab. Drei vorgeschlagene geschwindigkeitsbestimmende Mechanismen wurden zur Deutung der experimentellen Ergebnisse herangezogen, bei allen dreien blieben jedoch Probleme offen.
๐ SIMILAR VOLUMES
The activation energy, H, the activation volume, w\*, and the frequency factor, Y, for the plastic deformation of niobium at low temperatures (T < 0.2 T,) were derived from creep tests. The values of H and e\* for r\* = 1 kg/mm2 were 0.75 eV and 47bS respectively, decreasing with increase in stress.