Large-scale preparation of dispersive carbon nanotubes by arc-discharge method

โœ Scribed by Baohe Chang; Sishen Xie; Wenzhi Li; Chaoying Wang; Weiya Zhou; Luxi Qian; Lu Gan

Publisher
SP Science China Press
Year
1998
Tongue
English
Weight
590 KB
Volume
41
Category
Article
ISSN
1674-7283

No coin nor oath required. For personal study only.

๐Ÿ“œ SIMILAR VOLUMES

Large scale synthesis of single-wall car
Large scale synthesis of single-wall carbon nanotubes by arc-discharge method
โœ Zujin Shi; Yongfu Lian; Fu Hui Liao; Xihuang Zhou; Zhennan Gu; Y Zhang; S Iijima ๐Ÿ“‚ Article ๐Ÿ“… 2000 ๐Ÿ› Elsevier Science ๐ŸŒ English โš– 973 KB

Using a graphite rod with a hole filled with the powder of a mixture of Y-Ni alloy and graphite or calcium carbide and nickel as anode, single-wall carbon nanotubes (SWCNTs) with high yield were produced in quantity of tens of grams a day under the arc conditions of 40 ฯณ 60 A d.c. and helium pressur

Comparative Raman Study of Carbon Nanotu
Comparative Raman Study of Carbon Nanotubes Prepared by D.C. Arc Discharge and Catalytic Methods
โœ Pingheng Tan; Shu-Lin Zhang; Kwok To Yue; Fumin Huang; Zujing Shi; Xihuang Zhou; ๐Ÿ“‚ Article ๐Ÿ“… 1997 ๐Ÿ› John Wiley and Sons ๐ŸŒ English โš– 284 KB ๐Ÿ‘ 1 views

The Raman spectra of carbon nanotubes prepared by catalytic (C-CNT) and d.c. arc discharge (D-CNT) methods are reported. A previously unnoticed third-order Raman peak at ca. 4248 cm-1 was observed in the Raman spectrum of D-CNT. The Raman features of D-CNT and C-CNT are similar to those of highly or