Isothermal Ageing in the T Range from 0 "C to 180 "C of a Technical A1-2.0 at.% Zn-1.3 at.% Mg Alloy after Direct Quench
The variations of the structure and the mechanical properties had been investigated by means of TEM investigations and determination of the microhardness number in the T, range between 0 "C and 180 "C. The main results are the following: -At the starting period of the isothermal ageing an incubation time, tint, occurs. tint plotted versus T, yields two intersecting C curves at about 100 OC. -At T, = 70 "C the only decomposition product are G.P. zones. -At 70 "C < Ta < 100 "C the G.P. zones formed in the first period of decomposition can be transformed into (-phase or spherical hexagonal (S.H.) zones. -Above about 110 "C the precipitates present in the matrix are quasi-homogeneously formed a t nucleation sites delivered by clusters of impurity atoms. Die Veranderungen in der Struktur und in den mechanischen Eigenschaften wurden im Temperaturbereich T,, zwischen 0 "C und 180 "C mittels TEM-Untersuchungen und Bestimmung der Mikroharte untersucht. Die Hauptergebnisse sind die folgenden : -A111 Beginn der isothermen Alterung tritt eine Inkubationszeit, tint, auf. tint uber T, aufgetragen ergibt zwei sich bei etwa 100 "C schiieideiide C-Kurven. -Bei T , = 70 "C wachsen wahrscheinlich nur G.P.-Zonen. -I m T,-Bereich von 70 "C bis etwa 100 "C konnen die im ersten Eiitmischungsstadiurn gebildeten G.P.-Zonen in die (-Phase oder in spharische hexagonale (S.H.) Zonen ubergehen. -Oberhalb von etwa 110 "C werden die Ausscheidungen quasihomogen an bevorzugten Keimen (Clustern der Verunreinigungsatome) gebildet.