Investigations on the structure of fully hydrated portland cement and tricalcium silicate pastes. II. Total porosity and pore size distribution

✍ Scribed by I. Odler; H. Köster

Publisher
Elsevier Science
Year
1986
Tongue
English
Weight
419 KB
Volume
16
Category
Article
ISSN
0008-8846

No coin nor oath required. For personal study only.

📜 SIMILAR VOLUMES

Investigations on the structure of fully
Investigations on the structure of fully hydrated portland cement and tricalcium silicate pastes. I. Bound water, chemical shrinkage and density of hydrates
✍ H. Köster; I. Odler 📂 Article 📅 1986 🏛 Elsevier Science 🌐 English ⚖ 395 KB

On a series of fully hydrated OPC pastes hydrated at two temperatures (20 and 90 °C) and on tricalcium silicate pastes hydrated at 20 o the bound water, chemical shrinkage and density of hydrates were determined. Significant differences were found between the compared groups of materials with respec

Investigations on the relationship betwe
Investigations on the relationship between porosity, structure and strength of hydrated Portland cement pastes. II. Effect of pore structure and of degree of hydration
✍ I. Odler; M. Rößler 📂 Article 📅 1985 🏛 Elsevier Science 🌐 English ⚖ 424 KB

Cement pastes made with different water-cement ratios were hydrated at different temperatures for different times. The main factor influencing the strength properties of the obtained samples was found to be their porosity, however pores with radii of less than 10 nm affected the resultant strength o

Investigations on the relationship betwe
Investigations on the relationship between porosity structure and strength of hydrated portland cement pastes III. Effect of clinker composition and gypsum addition
✍ I. Odler; S. Abdul-Maula 📂 Article 📅 1987 🏛 Elsevier Science 🌐 English ⚖ 451 KB

In as series of cements made out of clinkers with variable C3A/C4AF ratios and containing different amounts of gypsum, the strength development and the composition of the hydrated material were studied. For a single clinker composition the obtained strength appears to be just a function of porosity.