Influence of Temperature and Long Term Ageing on the Fatigue Crack Growth in a Precipitation Hardened Martensitic Stainless Steel

โœ Scribed by Aboumou, L. Dimithe; Henaff, G.; Arzaghi, M.; Pommier, S.

Book ID
122184624
Publisher
Elsevier
Year
2013
Tongue
English
Weight
444 KB
Volume
66
Category
Article
ISSN
1877-7058

No coin nor oath required. For personal study only.

๐Ÿ“œ SIMILAR VOLUMES

Effects of R-ratio on high-temperature f
Effects of R-ratio on high-temperature fatigue crack growth behavior of a precipitation-hardening stainless steel
โœ Kuei-Chang Hsu; Chih-Kuang Lin ๐Ÿ“‚ Article ๐Ÿ“… 2008 ๐Ÿ› Elsevier Science ๐ŸŒ English โš– 486 KB

The high-temperature fatigue crack growth (FCG) behavior was investigated for a precipitation-hardening stainless steel, 17-4 PH, in three differently aged conditions. FCG tests were conducted at 400 and 500 ยฐC under various load ratios (R-ratios) ranging from R = 0.1 to 0.7. Results indicated the f

Crack closure and influence of cycle rat
Crack closure and influence of cycle ratio R on fatigue crack growth in type 304 stainless steel at room temperature
โœ H.U Staal; J.D Elen ๐Ÿ“‚ Article ๐Ÿ“… 1979 ๐Ÿ› Elsevier Science ๐ŸŒ English โš– 775 KB

Crack growth rate and crack closure during fatigue of type 304 stainless steel are measured with an optical microscope and television camera. Based on the crack closure data an effective stress intensity range AKFR is calculated. The da/da vs A&-curves indicate that crack closure could account for t