Influence of Ni on martensitic phase transformations in NiTi shape memory alloys
β Scribed by J. Frenzel; E.P. George; A. Dlouhy; Ch. Somsen; M.F.-X. Wagner; G. Eggeler
- Publisher
- Elsevier Science
- Year
- 2010
- Tongue
- English
- Weight
- 993 KB
- Volume
- 58
- Category
- Article
- ISSN
- 1359-6454
No coin nor oath required. For personal study only.
β¦ Synopsis
High-precision data on phase transformation temperatures in NiTi, including numerical expressions for the effect of Ni on M S , M F , A S , A F and T 0 , are obtained, and the reasons for the large experimental scatter observed in previous studies are discussed. Clear experimental evidence is provided confirming the predictions of Tang et al. 1999 [19] regarding deviations from a linear relation between the thermodynamic equilibrium temperature and Ni concentration. In addition to affecting the phase transition temperatures, increasing Ni contents are found to decrease the width of thermal hysteresis and the heat of transformation. These findings are rationalized on the basis of the crystallographic data of Prokoshkin et al. 2004 [68] and the theory of Ball and James . The results show that it is important to document carefully the details of the arc-melting procedure used to make shape memory alloys and that, if the effects of processing are properly accounted for, precise values for the Ni concentration of the NiTi matrix can be obtained.
π SIMILAR VOLUMES
In the binary system Ni-Ir it is known that Ni and Ir form a complete solid solution over the entire composition range. Starting from this, Ni 48.5-x Ti 51.5 Ir x alloys with x = 0, 2.5, 5 and 10 at.% and a Ni 49.5 Ti 48 Ir 2.5 alloy have been prepared by arc melting in an argon atmosphere in order
First-principles calculations are presented for parent B2 phase and martensitic B19 and B19 0 phases in NiTi. The results indicate that both B19 and B19 0 are energetically more stable than the parent B2 phase. By means of ab initio density functional theory, the complete distortion-shuffle energy l
The present paper considers the phase transition behavior of a single crystal Ni-rich NiTi alloy which was compression aged to produce one single family of Ni 4 Ti 3 precipitates. The single crystal material was produced in a two stage process. Polycrystalline material was first melted under an in