Influence of Cr-ions on the magnetic behaviour of FeCo film

✍ Scribed by Ratnesh Gupta; Raisa Ansari; Ashish Khandelwal; J. Fassbender; Ajay Gupta

• Book ID: 103862679
• Publisher: Elsevier Science
• Year: 2008
• Tongue: English
• Weight: 298 KB
• Volume: 266
• Category: Article
• ISSN: 0168-583X
• DOI: 10.1016/j.nimb.2007.12.065

✦ Synopsis

Implantation of Cr-ions in Fe 70 Co 30 thin film have been performed to modify its structural and magnetic properties. From the XRD results, the lattice constant as well as the grain size of the film is increasing with the ion fluence. Cr-ions (1 Â 10 17 ions/cm 2 ) reduces the coercivity of the film from 140(3) Oe to 44(3) Oe. Coercivity of the film follows the exponential decay as a function of Cr-ions fluence. 35 keV (projectile range 13.5 nm) and 100 keV Cr-ions (projectile range 34.3 nm) have been used to understand the effects of magnetic Cr-ions and the effects of ballistic collision cascade on the MOKE signal. Similar changes on the coercivity behaviour of the film implanted with these two energies have been observed. It appears that the implantation process creates a solid solution of Cr in FeCo without any other additional treatment in the film. After 5 Â 10 16 Cr-ions, film exhibit four fold magnetic anisotropy.