Influence of aluminium on the conversion of calcium silicate hydrate gels into 11 Å tobermorite at 90°C and 120°C
✍ Scribed by T. Mitsuda; H.F.W. Taylor
- Publisher
- Elsevier Science
- Year
- 1975
- Tongue
- English
- Weight
- 393 KB
- Volume
- 5
- Category
- Article
- ISSN
- 0008-8846
No coin nor oath required. For personal study only.
✦ Synopsis
Mixtures of Ca0 and colloidal silica with and without Y-A6203, CaO and alkali-bearing A6203-Si02 gels, or Ca0 and clinoptilolite
were treated hydrothermally at 90°C or 120°C for 4 hr -4 weeks.
Reaction seemed al~ays to proceed through formation of C-S-H gels to 11 A tobermorite.
In the absence of A6, tobermorite crystallized more rapidly at C/S = 1.0 than at C/S = 0.8, but in the presence of A6, it crystallized more rapidly at Ca/(Si + A6) = 0.8 than at Ca/(Si + A6) = 1.0.
Where the starting materials contained both A6 and alkali the tobermorite showed anomalous thermal behaviour similar to that of the natural mineral from Loch Eynort, but where they contained A6 but no alkali, the thermal behaviour of the tobermorite was complex.
Gemische von
CaO und kolloidalem SiO 2 mit und ohne Y-A6203, von Ca0 und alkalihaltigen A6203-Si02 Gelen, oder yon Ca0 und Klinoptilolit wurden 4 Stunden bis 4 Wochen lang bei 90°C oder 120°C hydrothermal behandelt. Die Reaktionoschien immer ~ber die Bildung yon C-S-H Gelen zu 11 A Tobermorit zu laufen.
In Abwesenheit yon A6, fief die Kristallisierung des Tobermorits schneller bei Ca/Si = 1,0 ale bei Ca/Si = 0,8, aber in Gegenwart von A6, schneller bei Ca/(Si + A6) = 0,8 ale bei Ca/(Si + A6) = 1,0.
Wenn des Ausgangsmaterial A6 und Alkali enthielt, zeigte des Tobermorit ein abnormales Thermalverhalten ~Lhnlich dem des nat~rlichen Minerals yon Loch Eynort.
Wenn aber des Ausgangsmaterial nur A6 und kein Alkali enthielt, war des Thermalverhalten des Produktes kompliziert.