Highly conducting and crystalline doubly doped tin oxide films fabricated using a low-cost and simplified spray technique

✍ Scribed by K. Ravichandran; G. Muruganantham; B. Sakthivel

• Publisher: Elsevier Science
• Year: 2009
• Tongue: English
• Weight: 278 KB
• Volume: 404
• Category: Article
• ISSN: 0921-4526
• DOI: 10.1016/j.physb.2009.08.017

✦ Synopsis

Doubly doped (simultaneous doping of antimony and fluorine) tin oxide films (SnO 2 :Sb:F) have been fabricated by employing an inexpensive and simplified spray technique using perfume atomizer from aqueous solution of SnCl 2 precursor. The structural studies revealed that the films are highly crystalline in nature with preferential orientation along the (2 0 0) plane. It is found that the size of the crystallites of the doubly doped tin oxide films is larger (69 nm) than that (27 nm) of their undoped counterparts. The dislocation density of the doubly doped film is lesser (2.08 Â 10 14 lines/m 2 ) when compared with that of the undoped film (13.2 Â 10 14 lines/m 2 ), indicating the higher degree of crystallinity of the doubly doped films. The SEM images depict that the films are homogeneous and uniform. The optical transmittance in the visible range and the optical band gap of the doubly doped films are 71% and 3.56 eV respectively. The sheet resistance (4.13 O/&) attained for the doubly doped film in this study is lower than the values reported for spray deposited fluorine or antimony doped tin oxide films prepared from aqueous solution of SnCl 2 precursor (without using methanol or ethanol).