High-temperature strength and ductility of L12-type Ni3Al-Ni3Mn intermetallic compound

โœ Scribed by N. Masahashi; T. Takasugi; O. Izumi

Publisher
Springer
Year
1987
Tongue
English
Weight
1000 KB
Volume
22
Category
Article
ISSN
0022-2461

No coin nor oath required. For personal study only.

๐Ÿ“œ SIMILAR VOLUMES

Mathematical and experimental investigat
Mathematical and experimental investigation of the self-propagating high-temperature synthesis (SHS) of TiAl3and Ni3Al intermetallic compounds
โœ H. Y. Sohn; X. Wang ๐Ÿ“‚ Article ๐Ÿ“… 1996 ๐Ÿ› Springer ๐ŸŒ English โš– 685 KB

One-dimensional mathematical modeling was used to describe the self-propagating high-temperature synthesis (SHS) process for preparing TiAI3 and NiaAI intermetallics. The kinetic parameters (activation energies and pre-exponential factors) for the two compounds were obtained by matching experimental

A Statistical-Thermodynamic Model for In
A Statistical-Thermodynamic Model for Intermetallic Phases with L12-Structure and Its Application to the Compound Ni3Al
โœ R. Krachler; O.P. Semenova; H. Ipser ๐Ÿ“‚ Article ๐Ÿ“… 1999 ๐Ÿ› John Wiley and Sons ๐ŸŒ English โš– 208 KB ๐Ÿ‘ 2 views

A statistical-thermodynamic model for binary nonstoichiometric L1 2 -phases has been developed based on a mean-field approximation. Vacancies and anti-structure atoms are allowed on both sublattices as possible point defects, and the expressions for the defect concentrations as functions of composit

Features of the microhardness near rando
Features of the microhardness near random and special type of boundaries in a Ni3Al intermetallic compound
โœ E.V. Konovalova; O.B. Perevalova; N.A. Koneva; E.V. Kozlov ๐Ÿ“‚ Article ๐Ÿ“… 2004 ๐Ÿ› Elsevier Science ๐ŸŒ English โš– 340 KB

Various types of the grain boundaries were identified in intermetallic compound Ni 3 Al polycrystals. Deviations from the stoichiometric composition were determined, and microhardness was measured inside the grains and at grain boundaries. Microhardness near special boundaries is smaller than near r