✦ LIBER ✦

High dose fast neutron irradiation of highly oriented pyrolytic graphite

✍ Scribed by B.T. Kelly; J.E. Brocklehurst

Publisher: Elsevier Science
Year: 1972
Tongue: English
Weight: 137 KB
Volume: 10
Category: Article
ISSN: 0008-6223
DOI: 10.1016/0008-6223(72)90472-1

No coin nor oath required. For personal study only.

📜 SIMILAR VOLUMES

High dose fast neutron irradiation of hi

High dose fast neutron irradiation of highly oriented pyrolytic graphite

✍ B.T. Kelly; J.E. Brocklehurst 📂 Article 📅 1971 🏛 Elsevier Science 🌐 English ⚖ 487 KB

Highly oriented samples of well graphitised pyrolytic graphite have been irradiated to doses of 2.5 X 102\* n.v.t. (Dido Equivalent Dose) at temperatures between 250°C and 470°C. Measurements have been made of the changes in dimensions parallel and perpendicular to the deposition planes, density, t

High-temperature neutron irradiation of

High-temperature neutron irradiation of highly oriented carbons and graphites

✍ R.J. Price 📂 Article 📅 1974 🏛 Elsevier Science 🌐 English ⚖ 918 KB

Highly oriented massive pyrolytic carbons were acnealed at, 2900-3300°C to produce apparent crystalline heights (L,) ranging from 220 A to 1660 A. Transmission electron microscopy showed that annealing progressively increased the crystallite width, while the height between twist boundaries was littl

The dimensional changes of highly-orient

The dimensional changes of highly-oriented pyrolytic graphite irradiated with fast neutrons at 430°C and 600°C

✍ J.E. Brocklehurst; B.T. Kelly 📂 Article 📅 1993 🏛 Elsevier Science 🌐 English ⚖ 382 KB

Samples of highly oriented graphite heat-treated to final temperatures of 2,000, 2,200, 2,400, 2,800 and 3,OOo"C have been successively irradiated with fast neutrons at controlled temperatures of430" and 600°C in the PLUTO Materials Testing Reactor. The dimensional changes of these samples, measured

Thermal annealing of pyrolytic graphite

Thermal annealing of pyrolytic graphite irradiated with fast neutrons at 40°C

✍ B.T. Kelly 📂 Article 📅 1969 🏛 Elsevier Science 🌐 English ⚖ 218 KB

107. Effects of high-temperature neutron

107. Effects of high-temperature neutron irradiation on highly oriented carbons and graphites

✍ R.J Price 📂 Article 📅 1969 🏛 Elsevier Science 🌐 English ⚖ 103 KB

observed etch-patterns seem to have no relation with the dislocation content of the crystals. The imphcations are discussed.

High temperature fast-neutron irradiatio

High temperature fast-neutron irradiation of pyrolytic-carbon-coated ThO2 microspheres

✍ D.M Hewette II 📂 Article 📅 1969 🏛 Elsevier Science 🌐 English ⚖ 828 KB

We determined the effects of fast-neutron damage aione on four types of pyrolytic-carbon coatings with spherical geometry. The coatings, which ranged in density from 1.75 to 2.0'7 g/cm" and had Bacon anisotropy factors from 1-O to 1.4, were irradiated in the Dounreay Fast Reactor to 4.5 X 102" neutr