Growth rate of yttria-stabilized zirconia thin films formed by electrochemical vapor-deposition using NiO as an oxygen source
✍ Scribed by Minoru Inaba; Atsushi Mineshige; Tomoyuki Maeda; Shinji Nakanishi; Tadayoshi Takahashi; Akimasa Tasaka; Kenji Kikuchi; Zempachi Ogumi
- Publisher
- Elsevier Science
- Year
- 1997
- Tongue
- English
- Weight
- 579 KB
- Volume
- 93
- Category
- Article
- ISSN
- 0167-2738
No coin nor oath required. For personal study only.
✦ Synopsis
Thin films of yttria-stabilized zirconia (YSZ) were formed onto nickel oxide substrates by an electrochemical vapor deposition process using the substrates as oxygen sources, and ZrCl, and YCl, as metal sources. After deposition at 1000°C for l-6 h, dense films of cubic YSZ were formed. The film thickness increased linearly with deposition time, and the linear growth rate constant was 1.1 X 10e4 pm s-l. The deposition kinetics were discussed, and it was concluded that the rate-determining step of this process is not the electrochemical transportation of the oxide ions and electrons through the growing film, but the mass transport of oxygen gas, which is dissociated from the NiO substrate, through the substrate pores to the NiO/YSZ interface.