Growth of Tetragonal Hausmannites MnxFe3−xO4 from Bi2O3-V2O5 Fluxes

✍ Scribed by Ing. Miloš Nevřiva; Ing. Pavel Holba

• Publisher: John Wiley and Sons
• Year: 1972
• Tongue: English
• Weight: 285 KB
• Volume: 7
• Category: Article
• ISSN: 0232-1300
• DOI: 10.1002/crat.19720071103

✦ Synopsis

Institute of Solid State l'liysics, Prague

Growth of Tetragonal Hausmannites RZn,Fe3 -=04 from Bi,O,-VV,O, Fluxes

Thegrowing of tetragonal single crystals of Mn,Pe3-.04 (z = 3.0 and 2.93) with hausmannite type structure is reported. Samplcs with x = 2.69 were no maro monocrystalline due to the cubic-tetragonal transformation. Crystals were grown at temperatures from 1150 to 950 "C from Bi20, + 10 wt.% V,O, melts. The largest crystals reached nearly 10 mm in length and weights till to 0.5 g.

Die Zuchtung von tetragonalen Einkristallen Mn,F3-,04 (z = 3,O und 2,93) mit Hausmannitstruktur wird beschrieben. Proben der Zusammensetzung z = 2,69 waren infolge der kubisch-tetragonalen Umwandlung nicht mehr einkristallin. Die Kristalle wurden aus einer Schmelze der Zusammensetzung Bi,O, + 10 Gew.yo V,O, im Temperaturintervall 1150-950 "C gezuchtet. Die grol3ten Exemplaro waren ungefiihr 10 mm grol3 und hatten ein Gewicht voii 0,5 g.