a b s t r a c t
In this study, the growth of a short edge crack during more than 14 000 cycles of fatigue loading is investigated in detail. An edge crack, in a semi-infinite body with no pre-existing obstacles present, is modelled in a boundary element approach by a distribution of dislocation dipoles. The fatigue cycles are fully reversed ðR ¼ À1Þ, and the load range is well below the threshold for long fatigue cracks. The developing local plasticity consists of discrete edge dislocations that are emitted from the crack tip. The movements of discrete dislocations are restricted to slip along preferred slip planes. The present model is restricted to a 2D plane strain problem with a through-thickness crack, assuming no 3D irregularities. A remote load is applied perpendicular to the crack extension line, and the material parameters are those of a BCC crystal structure. The competition between influence of the global loading on and local shielding of the crack tip governs the crack growth. The growth rate increases in discrete steps with short periods of retardation, from approximately the size of Burgers vector, b, up to 25 b per cycle as the length of the crack is tripled. The plastic zone changes from having an elongated, slender form to include a low angle grain boundary, which, eventually, divides into two parts. The crack growth is found to change from constant acceleration to constant growth rate as the event of the low-angle grain boundary split is approached. The results are compared to long crack characteristics, for which linear elastic fracture mechanics and Paris law can be used to predict fatigue crack growth. The exponent in Paris law varies between 1 and 0 in the present study, i.e. smaller than typical values for ductile BCC materials. The ratio between static and cyclic plastic zone sizes is found to increase during crack growth, and the angle of the general plastic zone direction increases, showing a tendency towards long crack values. The characteristics of the simulated crack growth, found in the present study, are typical for below-threshold growth, with slow acceleration, constant growth rate, and, eventually, either arrest or transition to long crack growth behaviour, as reported in the literature.