The growth kinetics of passive films on Fe, Fe-10 Ni, Fe10 Cr, Fe-10 Ni-10 Cr have been determin ed in pH 8.4 borate buffer solution at 25°C using ellipsometer and coulometric techniques. Films found on the alloys were progressively thinner as the alloy concentration was increased. The correlations with potential dependence suggest that the inverse logarithmic law may be applicable. The optical constants of the alloys in the film-free condition were similar but different from those of the films. The optical constants of the films on the alloys were similar.
R&um&D&ermina
tion a 25°C au moyen de techniques ellipsometrique et coulometrique de la vitesse de croissance des films passifs sur Fe, Fe-10 Ni, Fe-10 Cr, Fe-10 Ni-10 Cr dans une solution tampon&e au borate a pH 8,4. Les films form& sur les alliages s'amincissement progressivement quand la concentration en alliage augmente. Les correlations avec l'influence du potentiel suggerent que la loi logarithmique inverse peut 6tre applicable. Lcs constantes optiques des alliages exempts de film sont identiques, mais differentes de celles des films. Les constantes optiques des films sur les alliages ont et6 trouvees analogues.
Zusamntenfassung-Die
Wachstumskinetik passiver Schichten an Fe, Fe-10 Ni, Fe-10 Cr, Fe-10 Ni-10 Cr wurde mittels ellipsometrischer und coulometrischer Methoden in einer Boratpulferltisung (pH 8.4) bei 25°C untersucht. Die Schichten auf den Legierungen wurden mit steigender Legierungskonzentration dtinner. Der Zusammenhang mit der Potentialabhtigigkeit 1Psst annebmen, dass das inverse logarlthmlsche Gesetz anwendbar ist. Die opt&hen Konstanten der schichtfreien Legierungen waren ilhnlich aber verschieden von denjenigen der Schichten, welche untereinander iihnlich waren.