Fracture of Two-Layer Plates with Cracks in Tension with Regard for Local Buckling

✍ Scribed by M. Sh. Dyshel'

Book ID: 110402685
Publisher: Springer US
Year: 2002
Tongue: English
Weight: 142 KB
Volume: 38
Category: Article
ISSN: 1573-8922
DOI: 10.1023/a:1020986210394

No coin nor oath required. For personal study only.

📜 SIMILAR VOLUMES

Deformation of tensioned plates with cra

Deformation of tensioned plates with cracks with allowance for local buckling

✍ M. Sh. Dyshel'; M. A. Mekhtiev 📂 Article 📅 1987 🏛 Springer US 🌐 English ⚖ 398 KB

Buckling and cracking characteristics of

Buckling and cracking characteristics of two-layered plate in tension

✍ A.N Guz; M.Sh Dyshel 📂 Article 📅 2002 🏛 Elsevier Science 🌐 English ⚖ 108 KB

Biaxial tension of a homogeneous isotrop

Biaxial tension of a homogeneous isotropic plate with two equal coaxial cracks with regard for plastic zones near their tips

✍ M. M. Nykolyshyn; V. K. Opanasovych; L. R. Kurotchyn; M. S. Slobodyan 📂 Article 📅 2010 🏛 Springer US 🌐 English ⚖ 258 KB

Tensile fracture of plates with an edge

Tensile fracture of plates with an edge crack with allowance for preliminary local loss of stability

✍ M. Sh. Dyshel' 📂 Article 📅 1996 🏛 Springer US 🌐 English ⚖ 242 KB

Mixed mode fracture of a piezoelectric–p

Mixed mode fracture of a piezoelectric–piezomagnetic bi-layer structure with two un-coaxial cracks parallel to the interface and each in a layer

✍ Li, Yong-Dong; Zhao, Hao; Zhang, Nan 📂 Article 📅 2013 🏛 Elsevier Science 🌐 English ⚖ 691 KB

Inverse problem of material distribution

Inverse problem of material distribution for desired fracture characteristics in a thick-walled functionally graded material cylinder with two diametrically-opposed edge cracks

✍ A.M. Afsar; M. Anisuzzaman; J.I. Song 📂 Article 📅 2009 🏛 Elsevier Science 🌐 English ⚖ 396 KB

This study concerns the inverse problem of evaluating the optimum material distribution for desired fracture characteristics in a thick-walled functionally graded material (FGM) cylinder containing two diametrically-opposed edge cracks emanating from the inner surface of the cylinder. The thermal ei