Fracture of Ni-Ti superelastic alloy under sustained tensile load in physiological saline solution containing hydrogen peroxide
✍ Scribed by Ken'ichi Yokoyama; Toshio Ogawa; Atsushi Fujita; Kenzo Asaoka; Jun'ichi Sakai
- Publisher
- John Wiley and Sons
- Year
- 2007
- Tongue
- English
- Weight
- 572 KB
- Volume
- 82A
- Category
- Article
- ISSN
- 1549-3296
No coin nor oath required. For personal study only.
✦ Synopsis
Abstract
The fracture of Ni‐Ti superelastic alloy has been investigated by a sustained tensile‐loading test in physiological saline solution containing hydrogen peroxide (0.15__M__ NaCl + 0.3__M__ H~2~O~2~). The fracture always occurs when the applied stress exceeds the critical stress for martensite transformation. In contrast, under a low applied stress, the fracture does not always occur within 1000 h. The fracture is probably mainly caused by localized corrosion associated with the preferential dissolution of nickel ions. In 0.3__M__ H~2~O~2~ solution without NaCl, the fracture does not occur even under a high applied stress. The results of the present study imply that one reason for the fracture of the Ni‐Ti superelastic alloy in vivo is localized corrosion due to the synergistic effects of hydrogen peroxide and sodium chloride under applied stress. © 2007 Wiley Periodicals, Inc. J Biomed Mater Res, 2007