Formation of a -A1203 by Thermal Decomposition of Basic Aluminium Chlorides at Low Temperatures Basic aluminium chloride gels and the crystalline salt AIC1, . 2 Al(OH), . 6 H,O are thermally deconiposed to an amorphous product in a first step at low temperatures. I f the reaction gas is rapidly removed t h e amorphous decomposition product directly transforms t o corundum at increased temperature. Starting from gels the n-Al,O, formation begins at 420 "C, transformation of the crystalline salt at 530 "C. Structural similarities of precursor compounds and corundum are discussed as a reason for this behaviour. High contents of HC1 and H,O in the atmosphere surrounding the specimen result in dccomposition t o transition aluminas at increasing temperature, which are transformed into a-Al,O, above 1000 "C. Basische Alurniniumchloridgele und das kristalline basische Aluminiumchlorid AlCI, . x 2 AI(OH), . 6 H,O werden bei niedrigen Temperaturen zunachst zu einem amorphen Produkt thermisch zersetzt. Wenn die Zersetzungsgase schnell von der Probe abgefuhrt werden, geht das amorphe Abbauprodukt unmittelbar bei erhohter Temperatur in die Korundphase uber. Bei den Gelen beginnt die Korundbildung um 420 "C, bei den1 kristallinen Salz um 530 "C. Als Ursache fur dieses Verhalten werden strukturelle Ahnliclikeiten zwisclien Vorliiuferverbindungen und Korund diskutiert. Bei hohen Gehalten a n HC1 und H,O in der die Zersetzungsprobe umgebenden Atmosphiire verlLuft der Abbau bei steigender Teniperatur unter Bildung von Ubergangstonerden, die oberhalb 1000 "C in n-Al,O, ubergelien.
📜 SIMILAR VOLUMES