Abstract
We have observed that a highly protective amorphous aluminum silicate layer on a steel surface was formed after granite–dry steam interaction in the presence of a copper plate near the critical point of water. In this process, the mass transfer of aluminum and silicon species from the granite to the steel surface takes place after copper was transferred to the granite surface. The rate of this process is accelerated by the presence of copper on the granite surface. At present, we have determined the effect of transferred copper species on the weight loss of granite in dry steam with different ratios of O~2~ and N~2~. It was also found that transferred copper species at a low O~2~ level promote the weight loss of granite. Four types of experiments were conducted at low O~2~ ratios in different‐density steam: (1) steel–steam, (2) steel–Cu–steam, (3) steel–granite–steam, and (4) steel–granite–Cu–steam. It was established that an aluminum silicate film formed on the steel surface only at the steel–granite–Cu–dry steam interaction. The formed film was characterized by scanning electron microscopy equipped with energy‐dispersive X‐ray spectroscopy and by X‐ray photoelectron spectroscopy. (© 2006 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)