In powder mixtures of ZnO and Ti02 the compounds Zn2Ti04, ZnTiO3 and Zn2Ti308 can be formed as a result of solid state reactions. The mechanism of the double oxide formation is essentially determined by the microstructure of the powder mixture. Furthermore, the kind of the double oxide depends on the TiOrmodification. There exist structural similarities between Zn2TiOc (spinel) and Ti02 (anatase) on the one hand and ZnTiO3 and Ti02 (rutile) on the other hand. The compound ZnzTisOa is formed only on the basis of the ZnzTiO4-phase. The crystal structure of Zn2Ti308 was derived as a defect spinel. The unoccupied sites of cations are not arranged statistically, but they areprdered in the structure. This order leads to the decrease of the space group symmetry from Fd-3m to P4332.
In Pulvermischungen aus ZnO und Ti02 konnen Zn2Ti04, ZnTiOs and Zn2Ti308 entstehen. Der Mechanismus der Doppeloxidbildung wird wesentlich durch die Mikrostruktur der Pulvermischung bestimmt. Die Art des Doppeloxides hangt auhrdem von der Struktur der TiOrModifikation ab. Zwischen Zn2TiO4 (Spinell) und Ti02 (Anatas) einerseits und ZnTiO3 und Ti02 (Rutil) andererseits bestehen strukturelle Gemeinsamkeiten. Die Verbindung ZnzTi308 wird nur uber die Zwischenphase ZnzTiO4 gebildet. Die Kristallstruktur der Verbindung ZnzTi308 wurde als ein Defektspinell abgeleitet. Die unbesetzten Kationenpliitze liegen nicht ' statistisch, sondern geordnet i n der Struktur vor. Die Ordnung fiihrt zu einer Erniedrigung der Raumgruppensymmetrie von Fd-3m auf P4332.