Abstract
Collagen, as a major constituent of human connective tissues, has been regarded as one of the most important biomaterials. As a coating moiety on Ti hard‐tissue implants, the collagen has recently attracted a great deal of attention. This article reports the effects of fibrillar assembly and crosslinking of collagen on its chemical stability and the subsequent osteoblastic responses. The fibrillar self‐assembly of collagen was carried out by incubating acid‐dissolved collagen in an ionic‐buffered medium at 37°C. The degree of assembly was varied with the incubation time and monitored by the turbidity change. The differently assembled collagen was coated on the Ti and crosslinked with a carbodiimide derivative. The partially assembled collagen contained fibrils with varying diameters as well as nonfibrillar aggregates. On the other hand, the fully assembled collagen showed the complete formation of fibrils with uniform diameters of ∼100–200 nm with periodic stain patterns within the fibrils, which are typical of native collagen fibers. Through this fibrillar assembly, the collagen coating had significantly improved chemical stability in both the saline and collagenase media. The subsequent crosslinking step also improved the stability of the collagen coating, particularly in the unassembled collagen. The fibrillar assembly and the crosslinking of collagen significantly influenced the osteoblastic cell responses. Without the assembly, the collagen layer on Ti adversely affected the cell attachment and proliferation. However, those cellular responses were improved significantly when the collagen was assembled to fibrils and the assembly degree was increased. After crosslinking the collagen coating, these cellular responses were significantly enhanced in the case of the unassembled collagen but were not altered much in the assembled collagen. Based on these observations, it is suggested that the fibrillar assembly and the crosslinking of collagen require careful considerations in the collagen administration as a coating moiety. © 2005 Wiley Periodicals, Inc. J Biomed Mater Res, 2005