The influence of multiple overload at various stress intensity levels (AK) in the linear regime of Paris plot was studied in high strength low alloy structural steel SANH-55. It was observed that crack retardation increases by increasing the overload ratio and the number of overloads. Saturation eff
Centrally cracked specimens of JIS SM58Q and I-IT80 steels were fatigued. The fatigue crack growth rates, da/dn, and the stress intensity threshold levels, AK,, were measured over the range of stress ratio, R, from -1 to 0.8 by the use of an automatic method of continuously decreasing stress intensi
Ahabnet-The trend toward broader application of high-strength structural alloys has increased the potential for failure by low-cycle fatigue crack propagation. There is a signiBcant probability that complex structures will contain undetected cracks remaining from fabrication or that cracks will read