Fabrication of carbon-modified TiO2 nanotube arrays and their photocatalytic activity

✍ Scribed by Xiaoye Hu; Tianci Zhang; Zhen Jin; Junxi Zhang; Wei Xu; Jian Yan; Jinping Zhang; Lide Zhang; Yucheng Wu

Book ID: 113792398
Publisher: Elsevier Science
Year: 2008
Tongue: English
Weight: 583 KB
Volume: 62
Category: Article
ISSN: 0167-577X
DOI: 10.1016/j.matlet.2008.08.051

No coin nor oath required. For personal study only.

📜 SIMILAR VOLUMES

Synthesis of carbon-modified TiO2 nanotu

Synthesis of carbon-modified TiO2 nanotube arrays for enhancing the photocatalytic activity under the visible light

✍ Han Yang; Chunxu Pan 📂 Article 📅 2010 🏛 Elsevier Science 🌐 English ⚖ 813 KB

Fabrication of TiO2-coated magnetic nano

Fabrication of TiO2-coated magnetic nanoparticles on functionalized multi-walled carbon nanotubes and their photocatalytic activity

✍ Hongfu Zhou; Chen Zhang; Xiangdong Wang; Hangquan Li; Zhongjie Du 📂 Article 📅 2011 🏛 Elsevier Science 🌐 English ⚖ 967 KB

Fabrication and photocatalytic activity

Fabrication and photocatalytic activity of high-efficiency visible-light-responsive photocatalyst ZnTe/TiO2 nanotube arrays

✍ Yutang Liu; Xilin Zhang; Ronghua Liu; Renbin Yang; Chengbin Liu; Qingyun Cai 📂 Article 📅 2011 🏛 Elsevier Science 🌐 English ⚖ 930 KB

Fabrication and photocatalytic activity

Fabrication and photocatalytic activity of TiO2/SiO2composite nanotubes

✍ Zhen-Zhen Wang; Jin-Shu Wang; Hong-Yi Li; Guo-Song Sun; Ke-Lin Huang 📂 Article 📅 2011 🏛 Springer Netherlands 🌐 English ⚖ 510 KB

Fabrication of self-organized TiO2nanotu

Fabrication of self-organized TiO2nanotube arrays for photocatalytic reduction of CO2

✍ Ping, Guangxing; Wang, Chao; Chen, Da; Liu, Shu; Huang, Xiani; Qin, Laishun; Hua 📂 Article 📅 2013 🏛 Springer 🌐 English ⚖ 451 KB

Photoelectrochemical property and photoc

Photoelectrochemical property and photocatalytic activity of N-doped TiO2 nanotube arrays

✍ Jingjing Xu; Yanhui Ao; Mindong Chen; Degang Fu 📂 Article 📅 2010 🏛 Elsevier Science 🌐 English ⚖ 690 KB

N-doped TiO 2 nanotube arrays (NTN) were prepared by anodization and dip-calcination method. Hydrazine hydrate was used as nitrogen source. The surface morphology of samples was characterized by SEM. It showed that the mean size of inner diameter was 65 nm and wall thickness was 15 nm for NTN. The o