Experimental investigation of transient thermoelastic effects in dynamic fracture

✍ Scribed by D. Rittel

• Publisher: Elsevier Science
• Year: 1998
• Tongue: English
• Weight: 952 KB
• Volume: 35
• Category: Article
• ISSN: 0020-7683
• DOI: 10.1016/s0020-7683(97)00352-1

✦ Synopsis

Thermoelastic effects in fracture are generally considered to be negligible at the benefit of the conversion of plastic work into heat. For the case of dynamic crack initiation, the experimental and theoretical emphasis has been put on the temperature rise associated with crack-tip plasticity.

Nevertheless, earlier experimental work with polymers has shown that thermoelastic cooling precedes the temperature rise at the tip of a propagating crack (Fuller et al., 1975). Transient thermoelastic effects at the tip of a dynamically loaded crack have been theoretically assessed and shown to be significant when thermal conductivity is initially neglected (Rittel, 1997). However, the fundamental question of the relation between crack initiation and thermal fields, both of transient nature, is still open.

In this paper, we present an experimental investigation of the thermoelastic effect at the tip of fatigue cracks subjected to mixed-mode (dominant mode 1) dynamic loading. The material is commercial polymethylmethacrylate as an example of "brittle" material.

The applied loads, crack-tip temperatures and fracture time are simultaneously monitored to provide a more complete image of dynamic crack initiation. The corresponding evolution of the stress intensity factors is calculated by a hybrid-experimental numerical model.

The results show that substantial crack-tip cooling develops initially to an extent which corroborates theoretical estimates. This effect is followed by a temperature rise.

Fracture is shown to initiate during the early cooling phase, thus emphasizing the relevance of the phenomenon to dynamic crack initiation in this material as probably in other materials.