✍ Scribed by Hallensleben, Manfred L. ;Hoser, Wolfram F.
No coin nor oath required. For personal study only.
The radical polymerization of styrene was investigated in the presence of six different hydrazine derivatives. These compounds were selected in view of the nitrogen radicals, either from the aminyl or the hydrazyl type, resulting upon carbon radical attack. A distinct dependence of the rate of polymerization on the nature of hydrazine substituents was detected in thermally as well as radically (AIBN) induced polymerization. 1,2‐Diacetylhydrazine (13), 1,2‐bis(p‐nitrophenyl)hydrazine (16), 1,2‐diacetyl‐1,2‐diphenylhydrazine (15), and 1,2‐dimethylhydrazine (12) act as retarding compounds whereas 1,2‐diphenylhydrazine (14) and tetraphenylhydrazine (1) are inhibitors. The transfer constants were calculated from the Mayo equation to be 0,02 for 12, 0,06 for 13, 0,1 for 15, 0,8 for 16, 0,9 for 14, and 5,6 for 1. Any influence of polymerization temperature on the chain transfer constant was not observed. From model reactions only hydrazyl radicals were detected.
📜 SIMILAR VOLUMES
## Abstract Die Verzögerung der Polymerisation von Styrol durch verschieden substituierte Azobenzole wurde untersucht. Modellversuche ergaben, daß bei der Einwirkung der Zerfallsprodukte von Dibenzoylperoxid auf aromatische Azoverbindungen Hydrazylradikale entstehen, die ESR‐spektroskopisch nachgew
Die radikalische Polymerisation von Athylen und dessen Copolymerisation mit Vinylacetat und Vinylchlorid wurden untersucht. Die Ketteniibertragungskonstante durch das Monomere envies sich bei der Polymerisation von Athylen als vorn Druck abhlil?gig. Eine Druckabhangigkeit wurde auch fiir die Copolym