Effects of Ni additions and austenitizing temperature on secondary hardening behavior in high Co-Ni steels

✍ Scribed by H. R. Yang; K. B. Lee; H. Kwon

Publisher: The Minerals, Metals & Materials Society
Year: 2001
Tongue: English
Weight: 164 KB
Volume: 32
Category: Article
ISSN: 1073-5623
DOI: 10.1007/s11661-001-0213-8

No coin nor oath required. For personal study only.

📜 SIMILAR VOLUMES

Effects of Co and Ni on secondary harden

Effects of Co and Ni on secondary hardening and fracture behavior of martensitic steels bearing W and Cr

✍ H. Kwon; J. H. Lee; K. B. Lee; H. Kwon; C. M. Kim; H. R. Yang 📂 Article 📅 1998 🏛 The Minerals, Metals & Materials Society 🌐 English ⚖ 673 KB

Implication of elastic coherency in seco

Implication of elastic coherency in secondary hardening of high Co-Ni martensitic steels

✍ M. Grujicic 📂 Article 📅 1991 🏛 Springer 🌐 English ⚖ 532 KB

Effect of carbide precipitates on high t

Effect of carbide precipitates on high temperature creep of a 20Cr-25Ni austenitic stainless steel

✍ T. Yamane; Y. Takahashi; K. Nakagawa 📂 Article 📅 1984 🏛 Springer 🌐 English ⚖ 378 KB

Influence of substitution of cobalt for

Influence of substitution of cobalt for iron in 25Cr—20Ni austenitic stainless steels on high-temperature creep

✍ Toshimi Yamane; Kohei Suzuki 📂 Article 📅 1986 🏛 Springer 🌐 English ⚖ 152 KB

Effect of aluminium and silicon on high

Effect of aluminium and silicon on high temperature oxidation resistance of Fe-Cr-Ni heat resistant steel

✍ Haitao Wang; Qi Zhao; Huashun Yu; Zhenya Zhang; Hongwei Cui; Guanghui Min 📂 Article 📅 2009 🏛 Tianjin University 🌐 Chinese ⚖ 824 KB

High temperature wear and friction behav

High temperature wear and friction behaviour of 15Cr–15Ni–2Mo titanium-modified austenitic stainless steel in liquid sodium

✍ Hemant Kumar; V. Ramakrishnan; S.K. Albert; C. Meikandamurthy; B.V.R. Tata; A.K. 📂 Article 📅 2010 🏛 Elsevier Science 🌐 English ⚖ 881 KB

The sliding friction and wear behaviour of 15Cr-15Ni-2Mo titanium-modified austenitic stainless steel (alloy D9) was studied in high purity liquid sodium at high temperature viz. 473 and 823 K respectively using a reciprocating-type tribometer. Weight loss measured in specimens after the tests was n