Effects of temperature, initial stress i
โ
Nakasa Keijiro; Takei Hideo; Yoshida Motoharu
๐
Article
๐
1980
๐
Elsevier Science
๐
English
โ 951 KB
The relation between diffusion behavior of hydrogen atoms and crack branching in delayed failure was discussed. The hypotheses that diffusion paths of hydrogen atoms at crack tip broaden with increase of stress intensity factor K, and that crack branching occurs when hydrogen atoms diffuse through