Effect of prior history and asymmetry of the load cycle on threshold stress intensity factors of EP747 alloy

โœ Scribed by V. A. Gladkovskii; N. N. Vasserman; I. V. Sendyurev

Book ID
104911129
Publisher
Springer
Year
1989
Tongue
English
Weight
339 KB
Volume
25
Category
Article
ISSN
1573-885X

No coin nor oath required. For personal study only.

๐Ÿ“œ SIMILAR VOLUMES

Effects of temperature, initial stress i
Effects of temperature, initial stress intensity factor and loading speed on the crack branching in delayed failure
โœ Nakasa Keijiro; Takei Hideo; Yoshida Motoharu ๐Ÿ“‚ Article ๐Ÿ“… 1980 ๐Ÿ› Elsevier Science ๐ŸŒ English โš– 951 KB

The relation between diffusion behavior of hydrogen atoms and crack branching in delayed failure was discussed. The hypotheses that diffusion paths of hydrogen atoms at crack tip broaden with increase of stress intensity factor K, and that crack branching occurs when hydrogen atoms diffuse through

Effect of Material Combinations and Rela
Effect of Material Combinations and Relative Crack Size on the Stress Intensity Factors of Edge Interface Cracks
โœ X. Lan; N.A. Noda; Y. Zhang; K. Michinaka ๐Ÿ“‚ Article ๐Ÿ“… 2011 ๐Ÿ› Elsevier ๐ŸŒ English โš– 354 KB

In this paper, the stress intensity factors (SIFs) of a single edge interface crack in the bi-material bonded strip subjected to in-plane tension and bending moment are investigated systematically. The SIFs are computed for arbitrary material combinations with varying the relative crack size a/W. Sp