Effect of preparation methods on microstructures and microwave dielectric properties of Ba(Mg1/3Nb2/3)O3ceramics

✍ Scribed by Z. Q. Tian; H. Wang; W. J. Huang; C. Y. Zhang

Publisher
Springer US
Year
2007
Tongue
English
Weight
273 KB
Volume
19
Category
Article
ISSN
0957-4522

No coin nor oath required. For personal study only.

πŸ“œ SIMILAR VOLUMES

Dielectric properties of Pb(Mg1/3Nb2/3)O
Dielectric properties of Pb(Mg1/3Nb2/3)O3 and (Pb1βˆ’xLax)(Mg(1+x)/3Nb(2βˆ’x)/3)O3 ceramics prepared by columbite route
✍ Adelina Ianculescu; Ana BrΔƒileanu; Massimo Viviani; Liliana Mitoşeriu πŸ“‚ Article πŸ“… 2007 πŸ› Elsevier Science 🌐 English βš– 593 KB

The role of the La-addition on the A-site of the perovskite Pb(Mg 1/3 Nb 2/3 )O 3 (PMN) on the phase formation, microstructure and dielectric properties was investigated. Ceramic samples were obtained from PMN and (Pb 1-x La x )(Mg 1+x/3 Nb 2-x/3 )O 3 (PLMN) nanopowders synthesized by the columbite

Temperature and frequency dependence of
Temperature and frequency dependence of dielectric loss of Ba(Mg1/3Ta2/3)O3 microwave ceramics
✍ T. Shimada; K. Ichikawa; T. Minemura; T. Kolodiazhnyi; Jonathan Breeze; Neil McN πŸ“‚ Article πŸ“… 2010 πŸ› Elsevier Science 🌐 English βš– 431 KB

Ba(Mg 1/3 Ta 2/3 )O 3 ceramic possessing extremely high Q Γ— f value of more than 300 THz at microwave frequency was developed in our previous study. It is of great interest to understand the mechanism of microwave absorption in such a practical material. In the present study we report on the tempera

Sinterability improvement of Ba(Mg1/3Ta2
Sinterability improvement of Ba(Mg1/3Ta2/3)O3dielectric ceramics
✍ X. M. Chen; Y. Suzuki; N. Sato πŸ“‚ Article πŸ“… 1994 πŸ› Springer US 🌐 English βš– 387 KB

The sinterability of Ba(Mgl/3Ta2/3)O 3 ceramics synthesized by solid-state-reaction methods was investigated. The poor sinterability of the present ceramics was found to be primarily due to the presence of satellite secondary phases of BasTa4015 and Ba4Ta20 ~, and the nearly complete densification o