Effect of polarization on the corrosion cracking of Armco iron in acid solutions of hydrogen sulfide

✍ Scribed by V. A. Zaitsev; L. N. Lozhkin; V. V. Skorchelletti; G. M. Zavadskaya

Publisher: Springer
Year: 1977
Tongue: English
Weight: 153 KB
Volume: 12
Category: Article
ISSN: 1573-885X
DOI: 10.1007/bf00728204

No coin nor oath required. For personal study only.

📜 SIMILAR VOLUMES

Influence of inhibitors on the corrosion

Influence of inhibitors on the corrosion cracking resistance of 65g steel wire in hydrogen sulfide solutions

✍ A. P. Lubenskii; T. I. Sokolova 📂 Article 📅 1987 🏛 Springer 🌐 English ⚖ 164 KB

Effect of preliminary cyclic deformation

Effect of preliminary cyclic deformation and high-temperature heating on the resistance of Armco iron to corrosion cracking

✍ L. P. Kostiv; I. P. Vyval'; I. I. Dikii 📂 Article 📅 1976 🏛 Springer 🌐 English ⚖ 301 KB

Effect of cathodic polarization on the r

Effect of cathodic polarization on the rate of growth of cracks in corrosion cracking of high-strength steels in deaerated, aerated, and hydrogen-sulfide-saturated solutions of chlorides

✍ V. A. Marichev 📂 Article 📅 1977 🏛 Springer 🌐 English ⚖ 275 KB

Effect of inhibitors on corrosion cracki

Effect of inhibitors on corrosion cracking of high-strength steel in an aqueous solution of hydrogen sulfide

✍ A. K. Mindyuk; V. P. Koval'; I. I. Vasilenko; Yu. I. Babei 📂 Article 📅 1973 🏛 Springer 🌐 English ⚖ 134 KB

Influence of hydrogen absorption on the

Influence of hydrogen absorption on the corrosion cracking of steel 70 in acid solutions of thiocyanates

✍ V. A. Zaitsev; L. N. Lozhkin; V. V. Skorchelletti; L. R. Chesebieva 📂 Article 📅 1979 🏛 Springer 🌐 English ⚖ 148 KB

The effect of sulfide inclusions on the

The effect of sulfide inclusions on the susceptibility of steels to pitting, stress corrosion cracking and hydrogen embrittlement

✍ Prof. Dr. Z. Szklarska-śmialowska; Dr. E. Lunarska 📂 Article 📅 1981 🏛 John Wiley and Sons 🌐 German ⚖ 974 KB

## Abstract Recent opinions on the effect of nonmetallic inclusions, especially sulfides, on the nucleation of pits, stress corrosion cracks, and hydrogen‐induced cracks are reviewed. The nonmetallic inclusions present in steels as impurities adversely affect the corrosion resistance of steels. Th