In this paper we report some observations on the grain boundary internal friction peak in polycrystalline aluminium after neutron irradiation at low doses. On neutron irradiation the grain boundary peak has been depressed and shifted to lower temperature side. This effect can be explained in terms of rotation of interstitials in the dumb-bell configuration and their trapping by impurity atoms. On annealing, those impurity atoms segregate near the grain boundary region which depress the peak. INFLIJENCE DE L'IRRADIATION AUX NEUTROSS STR LE PIC DE FROTTEMENT INTERNE DES JOIXTS DE GRAIXS Ler, auteurs prPsentent quelques observations SUP le pit de frottement interne des joints de grains dans l'aluminium polycriatallin apr&s irradiation B faibles doses de neutrons. L'irradiation aux neutrons provoquo la diminution de l'amplitude du pit et le dPplace WI'S les tomp&atures d&xoissantes. Ceci peut &tre expliqui! par la rotation des inter&itiels dans la configuration de l'intrr&itiel dissocib et leur pibgeapn par lcs atomes d'impuretks. Au cows du recuit,, COB stomen d'impurrtPs se rawemblent. p&s des joints de grains et l'amplitude du pit diminue. DER EINFLUlj DER NEUTRONENBESTRAHLUNG AUF DAS KORNGRENZENMAXI3lUM DER INNEREN REIBUNG In dieser Arbeit berichten wir iiber einige Beobachtungen iiber das Korngrenzenmaximum der inneren Reibung in polykristallinem Aluminium nach Niedrigdosis-Neutronenbestrahlung. Durch die Neutronenbestrahlung wurde das Korngrenzenmaximum erniedrlgt und zu tiefen Temperaturen hin verschoben. Dieser Effekt, kann anhand der Drehung von Hantel-Zwischengitteratomen, die von Verunreinigungsatomen eingefangen wurden, erkliirt werden. Beim Anlasscn agglomerieren die Vcrunreinigungsatome an Korngrenzen und erniedrigen das Maximum.