Effect of ion irradiation induced defects on the excess conductivity of Cu1−xTlxBa2Ca1Cu2O8−δ superconductor thin films

✍ Scribed by A.A. Khurram; Nawazish A. Khan; Shakeel Ahmad; Ali Awais

Publisher
Elsevier Science
Year
2011
Tongue
English
Weight
488 KB
Volume
471
Category
Article
ISSN
0921-4534

No coin nor oath required. For personal study only.

📜 SIMILAR VOLUMES

AC-susceptibility measurements of Cu1−xT
AC-susceptibility measurements of Cu1−xTlxBa2Ca3Cu4O12−δ superconductor thin films with different thallium content
✍ Nawazish A. Khan; M. Mumtaz; A.A. Khurram; P. Kameli 📂 Article 📅 2008 🏛 Elsevier Science 🌐 English ⚖ 448 KB

We have studied the superconductivity of Cu 1Àx Tl x Ba 2 Ca 3 Cu 4 O 12Àd (x = 0.8 and 0.5) thin films by AC-susceptibility measurements under various external AC magnetic field strengths. It is observed from these measurements that the v 00 peak of AC-susceptibility measurements which is associate

Effects of post-annealing on the infrare
Effects of post-annealing on the infrared active phonon modes of low anisotropy (γ=5–11) Cu1−xTlxBa2Ca2Cu3O10−δ superconductor thin films
✍ Nawazish A Khan; A.A Khurram; M Mazhar 📂 Article 📅 2004 🏛 Elsevier Science 🌐 English ⚖ 451 KB

The effects of post-annealing conditions on the apical oxygen phonon modes have been investigated and their correlations with the critical temperature of the Cu 1Àx Tl x Ba 2 Ca 2 Cu 3 O 10Àd (Cu 1Àx Tl x -1223) superconductor thin films have been developed. The samples were annealed in different am

Temperature dependence of the millimeter
Temperature dependence of the millimeterwave conductivity of YBa2Cu3O7 and Bi2Sr2Ca1Cu2O8 Thin films at 300 GHZ
✍ U. Dähne; T. Amrein; Y. Goncharov; N. Klein; G. Kozlov; L. Schultz; N. Tellmann; 📂 Article 📅 1994 🏛 Elsevier Science 🌐 English ⚖ 170 KB

A millimeterwave spectrometer using continuously tunable backward wave oscillators as sources and a quasioptical interferometer in the Mach-Zehnder configuration was used to measure the transmittivity in amplitude and phase of 60nm thin YBa2Cu307 and 250nm thin Bi2Sr2CalCU208 films on NdGaO 3 substr