Three series of polyurethanes were prepared having 42 wt % hard segments based on 4,4Ј-dicyclohexyl methane diisocyanate (H 12 MDI) with trans,trans isomer contents in the 13 to 95 mol % range and 1,4-butanediol chain extender. The soft segments were based on macrodiols poly(hexamethylene oxide) (PH
Effect of chain extender structure on the properties and morphology of polyurethanes based on H12MDI and mixed macrodiols (PDMS–PHMO)
✍ Scribed by Raju Adhikari; Pathiraja A. Gunatillake; Simon J. Mccarthy; Gordon F. Meijs
- Publisher
- John Wiley and Sons
- Year
- 1999
- Tongue
- English
- Weight
- 226 KB
- Volume
- 74
- Category
- Article
- ISSN
- 0021-8995
No coin nor oath required. For personal study only.
✦ Synopsis
The effect of chain extender structure on properties and morphology of ␣,-bis(6-hydroxyethoxypropyl) polydimethylsiloxane (PDMS) and poly(hexamethylene oxide) (PHMO) mixed macrodiol-based aliphatic polyurethane elastomers was investigated using tensile testing, differential scanning calorimetry (DSC), and dynamic mechanical thermal analysis (DMTA). All polyurethanes were based on 50 wt % of hard segment derived from 4,4Ј-methylenecyclohexyl diisocyanate (H 12 MDI) and a chain extender mixture. 1,4-Butanediol was the primary chain extender, while one of 1,3bis(4-hydroxybutyl)tetramethyldisiloxane (BHTD), 1,3-bis(3-hydroxypropyl)tetramethyldisiloxane (BPTD), hydroquinonebis(2-hydroxyethyl)ether (HQHE), 1,3-bis(3-hydroxypropyl)tetramethyldisilylethylene (HTDE), or 2,2,3,3,4,4-hexafluoro-1,5-pentanediol (HFPD) each was used as a secondary chain extender. Two series of polyurethanes containing 80 : 20 (Series A) and 60 : 40 (Series B) molar ratios of primary and secondary chain extenders were prepared using one-step bulk polymerization. All polyurethanes were clear and transparent and had number-average molecular weights between 56,000 and 122,100. Incorporation of the secondary chain extender resulted in polyurethanes with low flexural modulus and high elongation. Good ultimate tensile strength was achieved in most cases. DSC and DMTA analyses showed that the incorporation of a secondary chain extender disrupted the hard segment order in all cases. The highest disruption was observed with HFPD, while the silicon-based chain extenders gave less disruption, particularly in Series A. Further, the silicon chain extenders improved the compatibility of the PDMS soft segment phase with the hard segment, whereas with HFPD and HQHE, this was not observed.
📜 SIMILAR VOLUMES
Two series of polyurethanes were prepared to investigate the effect of comacrodiol structure on properties and morphology of polyurethanes based on the siloxane macrodiol, ␣,-bis(6-hydroxyethoxypropyl) polydimethylsiloxane (PDMS). All polyurethanes contained a 40 wt % hard segment derived from 4,4Ј-
## Abstract A series of six polyurethanes were prepared to study the effect of silicon chain extender structure on properties and morphology of siloxane–polyurethanes. Polyurethanes were prepared by a two‐step bulk polymerization without a catalyst. The soft segment of the polyurethanes was based o
## Abstract A series of eight polyurethane elastomers was prepared using a two‐step bulk polymerization procedure to investigate the effect of the siloxane chain extender 1,3‐bis(4‐hydroxybutyl)1,1,3,3‐tetramethyldisiloxane (BHTD) on polyurethane properties and morphology. All polyurethanes were ba
A series of polycarbonate and copolycarbonate macrodiols was prepared by using an ester interchange reaction with ethylene carbonate and diols such as 1,6hexanediol, 1,10-decanediol, 2,2-diethyl-1,3-propanediol, 1,4-cyclohexanedimethanol, and 1,3-bis(4-hydroxybutyl)-1,1,3,3-tetramethyldisiloxane. Th