A mathematical model is formulated for solvent dissolution of rubbery and glassy polymers. An exact solution to the problem is derived for the constant diffusivity case, and a weighted residual solution is developed for the case of a concentrationdependent diffusion coefficient. The solution is used
Disentanglement and reptation during dissolution of rubbery polymers
โ Scribed by Balaji Narasimhan; Nikolaos A. Peppas
- Publisher
- John Wiley and Sons
- Year
- 1996
- Tongue
- English
- Weight
- 862 KB
- Volume
- 34
- Category
- Article
- ISSN
- 0887-6266
No coin nor oath required. For personal study only.
โฆ Synopsis
The dissolution mechanism of rubbery polymers was analyzed by dividing the penetrant concentration field into three regimes that delineate three distinctly different transport processes. The solvent penetration into the rubbery polymer was assumed to be Fickian. The mode of mobility of the polymer chains was shown to undergo a change a t a critical penetrant concentration expressed as a change in the diffusion coefficient of the polymer. It was assumed that beyond the critical penetrant concentration, reptation was the dominant mode of diffusion. Molecular arguments were invoked to derive expressions for the radius of gyration, the plateau modulus, and the reptation time, thus leading to a n expression for the reptation diffusivity. The disentanglement rate was defined as the ratio between the radius of gyration of the polymer and the reptation time. Transport in the second penetrant concentration regime was modeled to occur in a diffusion boundary layer adjacent to the polymer-solvent interface, where a Smoluchowski type diffusion equation was obtained. The model equations were numerically solved using a fully implicit finite difference technique. The results of the simulation were analyzed to ascertain the effect of the polymer molecular weight and its diffusivity on the dissolution process. The results show that the dissolution can be either disentanglement or diffusion controlled depending on the polymer molecular weight and the thickness of the diffusion boundary layer.
๐ SIMILAR VOLUMES
During supposedly isothermal sorption/desorption of gases or vapors by solid polymers, latent heat effects alter local temperatures with the result that diffusion behavior may appear to be non-Fickian. Even when sorption curves are seemingly Fickian, spurious values of the diffusion coefficient, D,
Steady state ยฏuorescence measurements have been used for studying the dissolution of polymer ยฎlms. These ยฎlms are formed by free radical polymerization of methyl methacrylate (MMA) in which pyrene (P y ) was introduced as a ยฏuorescence probe. Dissolution of poly(methyl methacrylate) (PMMA) ยฎlms in c
A dissolution pattern that indicates a solvent-mediated phase change is observed when aspirin crystals are dissolved in aqueous media. It is suggested that the phase change is caused by the crystallization of a less soluble form on the crystal surface during dissolution. The kinetic and thermodynami