The temperature dependence of reversible and irreversible portions of the magnetization was measured in polycrystalline nickel specimens. The temperature was varied between -196 and + 360"C, the hardness of the specimens by cold stretching. The reversible induction was measured by a mutual induction bridge (10 kHz), the irreversible part by BARKHAUSEN discontinuities ( m > 8 . cgs). The comparison of both contributions along the hysteresis loop yields characteristic properties of that part of magnetization and susceptibility, not covered by the measurements. Conclusions are drawn concerning the size distribution of unmeasurable small discontinuities.
~~ ~
Einleitung
Bei Untersuchungen uber den magnetischen BARKHAUSEN-Effekt ist es zur Beurteilung der Ergebnisse oft notwendig, den reversiblen Anteil der Magnetisierung zu kennen [l]. I n der Literatur findet man kaum Angaben hieriiber.
Vor allem fehlen systematische Untersuchungen in einem genugend groBen Temperaturbereich und bei gut definiertem Eigenspannungszustand des Materials. Wir haben daher an sehr reinem polykristallinem Nickel eine vollstiindige Magnetisierungsbilanz aufgestellt. Es wurde der reversible (x?), der differentielle (xd) und der BARKHAUSEN-(X,&hteil der SuszeptibilitLt zwischen -196 und