Dependence of the electrical resistance of intercalated graphite fibers on electric power

โœ Scribed by D.D.L. Chung; Lan W. Wong

Publisher
Elsevier Science
Year
1986
Tongue
English
Weight
236 KB
Volume
24
Category
Article
ISSN
0008-6223

No coin nor oath required. For personal study only.

โœฆ Synopsis

The electrical resistivity of graphite fibers intercalated with iodine monochloride was found to vary with the applied electric power, such that the electrical resistivity increased reversibly by up to 90% upon the application of electric power up to 7 x lo-' W/cm of a single fiber. The increase was most abrupt at a power of -4 X 1O-z W/cm.

๐Ÿ“œ SIMILAR VOLUMES

In-plane electrical resistivity of nitri
In-plane electrical resistivity of nitric acid intercalated graphite
โœ F.L. Vogel; H. Fuzellier; C. Zeller; E.J. McRae ๐Ÿ“‚ Article ๐Ÿ“… 1979 ๐Ÿ› Elsevier Science ๐ŸŒ English โš– 283 KB

Abstrret-Highly oriented pyrolytic graphite was intercalated with 100% concentrated nitric acid to the first, second, third and fourth stage. Electrical resistivity was measured normal to the "c" axis using two contactless r.f. induction methods in the I-100 kHz range. Whether the method used is eit

Electrical resistivity of fluorine-based
Electrical resistivity of fluorine-based intercalation compounds of graphite fiber in low temperature region
โœ T. Nakajima; B. Chang; T. Fujiwara; N. Watanabe; M. Endo ๐Ÿ“‚ Article ๐Ÿ“… 1988 ๐Ÿ› Elsevier Science ๐ŸŒ English โš– 267 KB

Temperature dependence of the resistivity has been measured between 4.2 K and 273 K on C,F, C,TiF, and C,VF,. The resistivity obeys the equation, p(T) = A + BT + CT\* in the temperature range up to around 170 K and 220 K, where C,F and C,VF, exhibit anomalous inflections possibly connected with phas

Electrical resistivity and magnetoresist
Electrical resistivity and magnetoresistance of carbon/graphite fibers intercalated with nitric acid and arsenic pentafluoride
โœ W.David Lee; Glenn P. Davis; F.Lincoln Vogel ๐Ÿ“‚ Article ๐Ÿ“… 1985 ๐Ÿ› Elsevier Science ๐ŸŒ English โš– 721 KB

series of high performance, experimental carbon/graphite fibers was intercalated and examined with respect to their metallic conductivity behavior by resistivity and magnetoresistance versus temperature measurements. One fiber was a polyacrylonitrile (PAN&type precursor and three were pitch base pr