Copolymers of polyoxymethylene were prepared from trioxane in the presence of conionomers such as dioxolane, 1,3-dioxane, dioxepane and epichlorohydrin, boron trifluoride etherate being used as catalyst. Fusion and crystallization phenomena were studied on these copolymers by use of density measurement, differential thermal analysis, dilatometry, and microscopy. The spherulite growth rate and the induction period of the crystallization were determined. The temperature dependence of the growth rate was calculated assuming a two-dimensional surface nucleation mechanism. la base d'un mecanisme de nucleation superficielle B deux dimensions.
Zusammenfassung
Copolymere von Polyoxymethylen wurden aus Trioxan in Gegenwart von Comonomeren wie Dioxolan, 1,3-Dioxan, Dioxepan und Epichlorhydrin rnit Borfluorid-Atherat als Katalysator dargestellt. Schrnelz-und Kristallisationserscheinungen wurden an diesen Polymeren durch Dichtemessungen, Differentialthermoanalyse, Dilatometrie, und Mikroskopie verfolgt. Die Wachstumsgeschwindigkeit der Spharolithe und die Induktionsperiode der Kristallisation wurden bestimmt. Die Temperaturabhiingigkeit der Wachstumsgeschwindigkeit wurde unter Annahme eines zweidimensionalen Oberflachenkeirnbildungsmechanismus berechnet.