Comparison of the effects of gamma radiation and low temperature hydrogen peroxide gas plasma sterilization on the molecular structure, fatigue resistance, and wear behavior of UHMWPE
✍ Scribed by Goldman, Marni ;Pruitt, Lisa
- Publisher
- John Wiley and Sons
- Year
- 1998
- Tongue
- English
- Weight
- 157 KB
- Volume
- 40
- Category
- Article
- ISSN
- 0021-9304
No coin nor oath required. For personal study only.
✦ Synopsis
The effects of gamma radiation and low temperature hydrogen peroxide gas plasma (HPGP) sterilization on structure and cyclic mechanical properties were examined for orthopedic grade ultra-high-molecular-weight polyethylene (UHMWPE) and compared to each other as well as to no sterilization (control). Density was monitored with a density gradient column and was found to be directly influenced by the sterilization method employed: Gamma radiation led to an increase, while plasma did not. Oxidation of the polymer was studied by observing changes in the carbonyl peak with Fourier transform infrared spectrometry and was found to be strongly affected by both gamma radiation and subsequent aging, while plasma sterilization had little effect. Gamma radiation resulted in embrittlement of the polymer and a decreased resistance to fatigue crack propagation. This mechanical degradation was a direct consequence of postradiation oxidation and molecular evolution of the polymer and was not observed in the plasmasterilized polymer. Both gamma radiation and plasma sterilization led to improved wear performance of the UHMWPE compared to the nonsterile control material.