Comparative study of aromatization selectivity during N-heptane reforming on sintered Pt/Al2O3 and Pt-Re/Al2O3 catalysts

✍ Scribed by Alfred A Susu

• Publisher: Wiley (John Wiley & Sons)
• Year: 2008
• Tongue: English
• Weight: 245 KB
• Volume: 83
• Category: Article
• ISSN: 0268-2575
• DOI: 10.1002/jctb.1894

✦ Synopsis

Abstract

BACKGROUND: The metal dispersed over a support can be present as small crystallites with sizes less than 5 nm. The smaller crystallites favour aromatization while larger crystallites favour cracking/hydrogenolysis. Sintering results in the agglomerization of smaller metal crystallites. Correlation of size with aromatization selectivity was investigated.

RESULTS: The primary products of n‐heptane reforming on fresh Pt were methane, toluene, and benzene, while on fresh Pt‐Re, the only product was methane. Both catalysts exhibited enhanced aromatization selectivity at different oxygen sintering temperatures. The reaction products ranged from only toluene at 500 °C sintering temperature to methane at a sintering temperature of 650 °C with no reaction at 800 °C for the Pt/Al~2~O~3~ catalyst. On Pt‐Re/Al~2~O~3~ catalyst, methane was the sole product at a sintering temperature of 500 °C while only toluene was produced at a sintering temperature of 800 °C.

CONCLUSION: This is the first time that sintering has been used to facilitate aromatization of supported Pt and Pt‐Re catalysts. A superior selectivity behaviour associated with bi‐metallic Pt catalysts is established. It was found that no reaction occurred on Pt catalyst after sintering at 800 °C whereas sintering Pt‐Re at 800 °C promoted aromatization solely to toluene. Copyright © 2008 Society of Chemical Industry