Combined chemical and mechanical effects on free radicals in UHMWPE joints during implantation

✍ Scribed by Jahan, M. S. ;Wang, C. ;Schwartz, G. ;Davidson, J. A.

• Publisher: John Wiley and Sons
• Year: 1991
• Tongue: English
• Weight: 1011 KB
• Volume: 25
• Category: Article
• ISSN: 0021-9304
• DOI: 10.1002/jbm.820250807

✦ Synopsis

An electron spin resonance (ESR) technique is employed to determine the free radical distribution in the articulating surfaces of retrieved acetabular cups and knee-joint plateaus (retrieved after more than 6 years of implantation). Similar measurements made on samples prepared from cyclically stressed and unstressed cups, and on samples following oxidations in nitric acid and intralipid solutions provided sufficient data to gain more knowledge about the combined chemical and mechanical effects on PE free radicals during implantation. In UHMWPE free radicals are primarily initiated by gamma-ray sterilization; however, during implantation, peroxy (scission type) free radicals are formed and reach a maximum concentration level (equilibrium state) due to oxidation by chemical (hemoglobin and/or synovial fluids) environment of the joints. Subsequently, due to frictional heating and stress in the loading zones, free radical reaction is accelerated and their number is reduced only in those areas. This is consistent with the observations of a temperature rise in acetabular cups during in nitro frictional wear stress tests and in vivo telemetry observations, as reported by others. Compared with the previously reported SEM micrographs the low-free-radical regions are correlated with high-wear areas and the high-freeradical regions with the low-wear areas.