Characterization of mechanically induced surface damage on the implant alloy TiAl6Nb7 in quasi-physiological media
✍ Scribed by C. Leinenbach; C. Fleck; D. Eifler
- Publisher
- John Wiley and Sons
- Year
- 2002
- Tongue
- English
- Weight
- 969 KB
- Volume
- 33
- Category
- Article
- ISSN
- 0933-5137
No coin nor oath required. For personal study only.
✦ Synopsis
To characterize mechanically induced surface damage scratch and rotating bending tests were performed on the implant alloy TiAl6Nb7 with different surface conditions (polished, thermally oxidized, anodically oxidized) in Hank's solution and in newborn calf serum at 37 8C. The surface processes taking place during repassivation or due to the fatigue loading were identified by measuring the free corrosion current and potential. Light and scanning electron microscopic investigations were used to correlate surface changes with the results of the electrochemical measurements.
Zur Charakterisierung mechanisch induzierter Oberfla Èchenscha Èden wurden Ritzversuche sowie Umlaufbiegeversuche an der Implantatlegierung TiAl6Nb7 mit unterschiedlichen Oberfla Èchenzusta Ènden (poliert, thermisch oxidiert, anodisch oxidiert) in Hanklo Èsung bzw. in Ka Èlberserum bei 37 8C durchgefu Èhrt. Die wa Èhrend der Repassivierung bzw. aufgrund der Ermu Èdungsbeanspruchung an der Oberfla Èche ablaufenden Prozesse wurden durch Messung des freien Korrosionstroms bzw. Korrosionspotentials erfasst. Mit Hilfe licht-und rasterelektronenmikroskopischer Verfahren wurden die durch Ritzen eingebrachten bzw. ermu Èdungsbedingten Oberfla Èchenvera Ènderungen sowie deren Wechselwirkung mit den physiologischen Medien mit den Ergebnissen der elektrochemischen Messungen korreliert.