Cavitation erosion resistance of Cr–N coating deposited on stainless steel

✍ Scribed by Alicja Krella; Andrzej Czyżniewski

• Publisher: Elsevier Science
• Year: 2006
• Tongue: English
• Weight: 727 KB
• Volume: 260
• Category: Article
• ISSN: 0043-1648
• DOI: 10.1016/j.wear.2005.09.018

✦ Synopsis

Results of investigation on cavitation-erosion resistance of Cr-N coating deposited on stainless steel X6CrNiTi18-10 (1H18N9T) by means of the cathodic-arc method are presented. The evaluation of Cr-N coating resistance to cavitation erosion is based on the investigation performed in a cavitation tunnel with a slot cavitator and tap water as a medium. The investigation was performed at variable-cavitation intensity and the estimated cavitation resistance parameters of coatings were the incubation period of damage and the instantaneous erosion rate after exposure of specified duration. It has been confirmed that the incubation period of the Cr-N coating damage is approximately 50% longer than that of the uncoated X6CrNiTi18-10 steel, and the instantaneous erosion rate after exposure of specified duration is comparable in both cases. The scanning microscope analysis indicates that the damage of Cr-N coating is due mainly to its delamination, while the erosion of deeper parts of the coating is of minor importance. The character of the coating and substrate damage in multiple locations indicates that the hard coating microparticles torn-off during the cavitation bubbles implosion hit against the coating and the revealed areas of substrate. As a result, the coating and especially the substrate of relatively low hardness are subject to cavitation erosion and to solid particle erosion with the hard torn-off microparticles of coating. The results of the investigation and the analysis indicate that the factors mainly responsible for a long incubation period and low cavitation erosion rate of the steel substrate/hard coating systems are the gained high hardness of substrate and high level of coating adhesion.