In the solid state the Si-Cr-Cu system shows a three phase equilibrium between a Cr-rich b.c.c. phase and two f.c.c. phases rich in Ni and in Cu respectively.
This rather unexpected feature (Xi and Cu being caompletely miscible) is examined thermodynamically, using the regular approximation.
The most probable values of the interaction parameters are obtained from data on the binary boundary s;stpnls. The resulting ternary diagram is indeed of the type found experimentally. DEDUCTION DU DIAGRAIKME DE PHASE Ni-Cr-Cu $ PARTIR DI< RfiSULTATS BINAIRES A 1'6tat solide, le systBme Ni-Cr-Cu prCsente un Bquilibre ternairn entre une phase C.C. riche en rhrome et deux phases c.f.c. riches respectivemont en nickel et cuivre. Cet &tat de chases, plutBt inattendu (le nickel et le cuivre &ant compli?tement miscibles) est exnmini: thermodynamiquement en utilisant une approximation normale. Les valeurs les plus probables pour les paramktres d'interaction sont obtenues B partir de don&es SUP les systemes binaires. Le diagramme tcrnnire r&s&ant rst bien de la m&e formu que cellc, trouv&: ~~xp&iment,alernent. RER.ECHNUNG DES Ni-Cr.Cu.ZUSTANDSDIrlGnAMMS AUS ERGEBNISSEN AN BIN&ES SYSTEJIEN Im fest,en Zustand zeigt das System Ni-Cr.Cu oin Dreiphasengleichgewicht zwischen eincr cbromreichen kubisch raumzentrierten Phase und zwei Cu.bzw. Xi-reichen kubisch fliichenzentrierten Phasen. Diese, angesichts der vollst&ndigen gegenseitigen Mischbarkeit von Ni und Cu unerwartete Erscheinung wird thermodynamisch untersucht in der regulgren N&herung. Die wahrscheinlichstcn \Veert,e dcr Wechselwirkungsparameter werden Ergebnissen an den biniiren Grenzsystemen entnommen. Das dnmit herechneto tern&o Znstandsdiagramm entspricht dem experiment,& gefundenen.