The role of calcium in the mechanical strength of isolated cell walls of soybean (Glycine max (L.) Merr. cv. Wayne) hypocotyls has been investigated, using the Instron technique to measure the plastic extensibility (PEx) of methanolboiled, bisected hypocotyl sections and epidermal strips, and atomic absorption spectroscopy to measure wall calcium. Plastic extensibility was closely correlated with the growth rate of intact soybean hypocotyls. Removal of calcium from isolated cell walls by ethylene glycol-bis(2-aminoethyl ether)-N,N,N',N'-tetraacetic acid (EGTA) or low pH increased PEx, while addition of calcium decreased PEx; both effects were reversible. The amount of calcium removed and the increase in PEx at pH 4.5 were strongly dependent upon the chelating ability of the buffer anion. There was a direct correlation between the amount of calcium removed from the wall by EGTA or acid and the increase in PEx. Removal of up to 60% of the calcium increased PEx of half-sections up to two fold, but further loss of calcium caused a much greater increase in PEx. With epidermal strips, PEx increased only when calcium was reduced below a threshold. At pH 3.5, there was an additional increase in PEx after a lag of about 2 h; this additional increase may be the result of acid-induced cleavage of a different set of load-bearing bonds. We conclude that calcium bridges are part of the load-bearing bonds in soybean hypocotyl cell walls, and that breakage of these crosslinks by apoplastic acid participates in wall loosening. Acid-induced solubilization of wall calcium may be one mechanism involved in wall loosening of dicotyledonous stems.